Fatigue Behaviour and Crack Initiation in CoCrFeNiMn High-Entropy Alloy Processed by Powder Metallurgy.
Metals. Roč. 9, č. 10 (2019), č. článku 1110. ISSN 2075-4701. E-ISSN 2075-4701
Grant CEP: GA ČR(CZ) GA17-23964S
Institucionální podpora: RVO:68081723 ; RVO:61389021
Klíčová slova: high entropy alloy * microstructure * spark plasma sintering * fatigue * grain size
Obor OECD: Materials engineering; Materials engineering (UFP-V)
Impakt faktor: 2.117, rok: 2019
Způsob publikování: Open access
Web výsledku:
https://www.mdpi.com/2075-4701/9/10/1110/htm
DOI: https://doi.org/10.3390/met9101110

Oxide dispersion-strengthened (ODS) materials contain homogeneous dispersions of temperature-stable nano-oxides serving as obstacles for dislocations and further pinning of grain boundaries. The strategy for dispersion strengthening based on complex oxides (Y-Hf, -Zr, -Ce, -La) was developed in order to refine oxide dispersion to enhance the dispersion strengthening effect. In this work, the strengthening of EUROFER steel by complex oxides based on Y and elements of the IIIB group (lanthanum, scandium) and IVB group (cerium, hafnium, zirconium) was explored. Interparticle spacing as a dispersoid characteristic appeared to be an important factor in controlling the dispersion strengthening contribution to the yield strength of ODS EUROFER steels. The dispersoid size and average grain size of ODS EUROFER steel were altered in the ranges of 5–13 nm and 0.6–1.7 m, respectively. Using this strategy, the yield strength of the prepared alloys varied between 550 MPa and 950 MPa depending on the doping element.