Interplay of slip and twinning in niobium single crystals compressed\nat 77 K

0496930 - ÚFM 2019 RIV US eng J - Článek v odborném periodiku
Gröger, Roman - Chlup, Zdeněk - Kuběnová, Tereza - Kuběna, Ivo
Interplay of slip and twinning in niobium single crystals compressed
at 77 K.
Journal of Materials Research. Roč. 34, č. 2 (2019), s. 261-270. ISSN 0884-2914. E-ISSN 2044-5326
Grant CEP: GA ČR(CZ) GA16-13797S; GA MŠMT(CZ) LQ1601
Institucionální podpora: RVO:68081723
Klíčová slova: niobium * slip * twinning * 77 K * plasticity
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 2.502, rok: 2019

High-purity niobium single crystals of five different orientations were compressed at 77 K to
2–4% plastic strain to investigate the mechanisms operative in the initial stage of yielding. The
crystals deformed in the direction close to the [001] axis exhibit predominant slip on the highstressed
(101) and a much lower stressed ð0 11Þ plane. The expected slip on the ð 101Þ plane is
nearly homogeneously distributed with only a few sharp slip traces corresponding to localized
slip. The samples compressed along center-triangle orientations and those close to the
½011 ½ 111 edge deform predominantly by twinning on {112}h111i systems with some
contribution from slip on the ð 101Þ½ 1 1 1 system with the highest Schmid factor. A majority of
twins exhibit internal contrast due to alternating slip on ð 101Þ and ð0 11Þ planes. No slip traces are
observed in the matrix adjacent to the twin, which implies that twin boundaries are impenetrable
obstacles for the motion of dislocations.