Dislocation dissociations in C11.sub.b./sub. MoSi.sub.2./sub. and their impact on its plastic deformation
- 1.0490262 - FZÚ 2019 RIV GB eng J - Článek v odborném periodiku
Paidar, Václav - Čák, M. - Šob, Mojmír - Vitek, V.
Dislocation dissociations in C11.sub/sub. MoSi2 and their impact on its plastic deformation.
Intermetallics. Roč. 97, Jun (2018), s. 34-41. ISSN 0966-9795. E-ISSN 1879-0216
Grant CEP: GA ČR(CZ) GA16-14599S; GA ČR(CZ) GA16-24711S; GA MŠMT(CZ) LQ1601
Institucionální podpora: RVO:68378271 ; RVO:68081723
Klíčová slova: hexagonal metals * mechanical properties * twinning
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 3.353, rok: 2018
Using the DFT calculated gamma-surfaces possible metastable stacking faults have been found for the most common slip planes {013) and {110) in MoSi2. These calculations reveal three distinct stacking faults on {013) planes and one stacking fault on {110) plane. Owing to such multiplicity of metastable stacking faults there is a large number of possible dislocation dissociations. These dislocation splittings are analysed using the anisotropic elasticity and relevant stacking faults. The results show that the only dissociations of the < 331] dislocations favoured over the complete undissociated dislocations are on {013) planes either in one or two planes of this type. Splitting into {110) planes are never favoured. For the screw dislocation the dissociations on {013) planes lead to configurations that are sessile and block the dislocations glide in the case of compression along the [001] axis. This explains why for this orientation of compressive axis the single crystals are brittle at ambient temperature but dislocation glide may occur for compressive loading along different, less symmetrical directions.