Effect of rheological characteristics of polyethylene oxide on the electrospinning

0489426 - ÚH 2019 RIV IT eng A - Abstrakt
Peer, Petra - Zelenková, Jana - Polášková, M. - Filip, Petr
Effect of rheological characteristics of polyethylene oxide on the electrospinning.
Annual European Rheology Conference. Naples: The European Society of Rheology, 2018. s. 166.
[Annual European Rheology Conference /12./, Meeting of the Italian Society of Rheology /15./. 17.04.2018-20.04.2018, Sorrento]
Grant CEP: GA ČR GA17-26808S
Institucionální podpora: RVO:67985874
Klíčová slova: polyethylene oxide (PEO) * nanofibrous webs * molecular weight (MW) * diameter of fibres
Obor OECD: Fluids and plasma physics (including surface physics)

The effects of average molecular weight (MW) on the fibre diameter of electrospun polyethylene oxide (PEO) have been investigated. PEO with molecular weights ranging from 100 000 to 1 000 000 g/mol was dissolved in distilled water at various concentrations. The rheological properties especially the elasticity of polymer solution were measured and correlated with average fibre diameter. It was observed that the elasticity of PEO aqueous solutions increased with increasing MW whereas the viscosity was kept fixed. Nanofibrous webs obtained at optimal conditions were analysed by means of a scanning electron microscope. The diameter of fibres with circular cross sections increased with elasticity of polymer solution.