Pressure pipe damage: Numerical estimation of point load effect

0485029 - ÚFM 2018 RIV CH eng C - Konferenční příspěvek (zahraniční konf.)
Zouhar, Michal - Hutař, Pavel - Ševčík, Martin - Náhlík, Luboš
Pressure pipe damage: Numerical estimation of point load effect.
Key Engineering Materials. In: Advances in Fracture and Damage Mechanics XI. Zurich: Trans Tech Publications, 2013 - (Qingfen, L.; Yulong, L.; Aliabadi, M.), Roč. 525-526 (2013), s. 177-180. Key Engineering Materials, 525-526. ISBN 978-3-03785-463-1. ISSN 1013-9826.
[FDM 2012 - International Conference on Fracture and Damage Mechanics /11./. Xian (CN), 12.09.2012-18.09.2012]
Grant CEP: GA ČR(CZ) GAP108/12/1560; GA ČR(CZ) GD106/09/H035
Institucionální podpora: RVO:68081723
Klíčová slova: slow crack-growth * failure * polymer pressure pipes * point load * stress intensity factor * crack shape prediction
Obor OECD: Audio engineering, reliability analysis

The most relevant loading conditions for real polymer pipe systems are not only internal pressure, but also loading caused by sand embedding including bending or different kinds of point loads. It has been shown that service lifetime of buried pipes can be reduced especially due to stress concentration caused by external point loads. If the pipe is loaded locally the stress is concentrated here and a crack can initiate at this position or the existing crack can be affected by corresponding stress redistribution. In the paper the effect of the hard indenter, Poisson's ratio, hoop stress level and pipe wall thickness on the crack shape was estimated using numerical simulations of the creep crack propagation based on finite element method. Relation between crack length and crack width was found and expressed by simple relationship. A deeper understanding of the point load effect in order to prevent unexpected failure of the pipelines is of paramount importance for pipeline design.