2 inch size Czochralski growth and scintillation properties of Li.sup.+./sup.-co-doped Ce:Gd.sub.3./sub.Ga.sub.3./sub.Al.sub.2./sub.O.sub.12./sub.
- 1.0482726 - FZÚ 2018 RIV NL eng J - Článek v odborném periodiku
Kamada, K. - Shoji, Y. - Kochurikhin, V.V. - Yoshino, M. - Okumura, S. - Yamamoto, S. - Yeom, J.Y. - Kurosawa, S. - Yokota, Y. - Ohashi, Y. - Nikl, Martin - Yoshikawa, A. … celkem 13 autorů
2 inch size Czochralski growth and scintillation properties of Li+-co-doped Ce:Gd3Ga3Al2O12.
Optical Materials. Roč. 65, Mar (2017), s. 52-55. ISSN 0925-3467. E-ISSN 1873-1252
Grant CEP: GA ČR GJ15-18300Y
GRANT EU: European Commission(XE) 644260 - INTELUM
Institucionální podpora: RVO:68378271
Klíčová slova: scintillator * garnet * single crystal * crystal growth
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 2.320, rok: 2017
The 2 inch size Li 0.15 and 1.35 mol% co-doped Ce:Gd3Al2Ga3O12 single crystals were prepared by the Czochralski (Cz) method. Absorption and luminescence spectra were measured together with several other scintillation characteristics, namely the scintillation decay and light yield to reveal the effect of Li co-doping. Ce4+ CT absorption below 350 nm is clearly enhanced by Li co-doping as same as divalent ions co-doping. By 1.35 at.% Li co-doping, light yield was decrease to 88% of the Ce: GAGG standard and decay time was accelerated to 34.3ns 21.0%, 84.6ns 68.7%, 480ns 10.3%. The timing resolution measurement for a pair of 3 x 3 x 3 mm3 size Li,Ce:GAGG scintillator crystals was performed using Si-PMs and the timing resolution of the 1.35 at.% Li co-doped Ce:GAGG was 218ps