Grain boundary segregation of elements of groups 14 and 15 and its consequences for intergranular cohesion of ferritic iron.
Journal of Materials Science. Roč. 52, č. 10 (2017), s. 5822-5834. ISSN 0022-2461. E-ISSN 1573-4803
Grant CEP: GA ČR GAP108/12/0144; GA MŠMT(CZ) LQ1601
Institucionální podpora: RVO:68378271 ; RVO:68081723
Klíčová slova: grain boundary segregation * segregation enthalpy * intergranular fracture * strengthening/embrittling energy
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 2.993, rok: 2017

The experimentally determined data—enthalpy and entropy—of the grain boundary segregation of substitutional solutes of 14th and 15th groups of the periodic table, i.e., silicon, phosphorus, tin, and antimony, in a-iron are compared. The consequences of the grain boundary segregation of these elements for the intergranular strengthening or embrittlement are also shown. It is documented that all these solutes except silicon segregate at the grain boundaries interstitially at enhanced temperatures although substitutional segregation is preferred at zero K. Despite some variations, the values of the strengthening/ embrittling Gibbs energy of all solutes are nearly linearly dependent on the differences in the sublimation energies of the host and solute.