Spark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties

0468777 - ÚFP 2017 RIV CH eng J - Článek v odborném periodiku
Molnárová, O. - Málek, P. - Lukáč, František - Chráska, Tomáš
Spark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties.
Materials. Roč. 9, č. 12 (2016), č. článku 1004. E-ISSN 1996-1944
Grant CEP: GA ČR(CZ) GA15-15609S
Institucionální podpora: RVO:61389021
Klíčová slova: gas atomized Al7075 alloy * spark plasma sintering * microstructure * microhardness * high temperature stability
Kód oboru RIV: JJ - Ostatní materiály
Impakt faktor: 2.654, rok: 2016
http://www.mdpi.com/1996-1944/9/12/1004

The powder of an Al7075 alloy was prepared by gas atomization. A combination of cellular, columnar, and equiaxed dendritic-like morphology was observed in individual powder particles with continuous layers of intermetallic phases along boundaries. The cells are separated predominantly by high-angle boundaries, the areas with dendritic-like morphology usually have a similar crystallographic orientation. Spark plasma sintering resulted in a fully dense material with a microstructure similar to that of the powder material. The continuous layers of intermetallic phases are replaced by individual particles located along internal boundaries, coarse particles are formed at the surface of original powder particles. Microhardness measurements revealed both artificial and natural ageing behavior similar to that observed in ingot metallurgy material. The minimum microhardness of 81 HV, observed in the sample annealed at 300 °C, reflects the presence of coarse particles. The peak microhardness of 160 HV was observed in the sample annealed at 500 °C and then aged at room temperature. Compression tests confirmed high strength combined with sufficient plasticity. Annealing even at 500 °C does not significantly influence the distribution of grain sizes—about 45% of the area is occupied by grains with the size below 10 µm.