SEM and SEM by EDX analysis of air-processed SmBa.sub.2./sub.Cu.sub.3./sub.O.sub.y./sub.

  1. 1.
    0466298 - FZÚ 2017 RIV NL eng C - Konferenční příspěvek (zahraniční konf.)
    Kasuga, K. - Muralidhar, M. - Diko, P. - Jirsa, Miloš - Inoue, K. - Murakami, M.
    SEM and SEM by EDX analysis of air-processed SmBa2Cu3Oy.
    Physics Procedia, Vol. 81. Amsterdam: Elsevier, 2016 - (Tanabe, K.; Amemiya, N.), s. 41-44. ISSN 1875-3884.
    [International Symposium on Superconductivity /28./. ISS 2015. Tokyo (JP), 16.11.2015-18.11.2015]
    Institucionální podpora: RVO:68378271
    Klíčová slova: SmBaCuO * air process * SEM * SEM by EDX * critical current density
    Kód oboru RIV: BM - Fyzika pevných látek a magnetismus

    The present investigation focuses on the microstructure and chemical analysis of the in-air processed SmBa2Cu3Oy (Sm-123) sample with 3 wt% BaO2 and 20 wt% Ag2O addition. DC magnetization measurements showed a sharp superconducting transition with onset Tc at around 94.5 K. The critical current density (Jc) at 77 K and zero field was 24 kA/cm2. SEM analysis indicated dispersion of submicron secondary phase particles in the Sm-123 matrix. SEM by EDX analysis confirmed that matrix chemical ratio at various locations of the pellet was uniform. Trapped magnetic field profile analysis confirmed that samples were single grain. The sample with size of 12 by 12 mm and 5 mm thickness showed the trapped field on top surface 0.26T at liquid nitrogen temperature. The
    results indicate that content of BaO2 is crucial for improving utilization parameters of the bulk Sm-123 material melt-processed in air.