Damage Evolution in Thermomechanical Loading of Stainless Steel

  1. 1.
    0465508 - ÚFM 2017 RIV NL eng C - Konferenční příspěvek (zahraniční konf.)
    Petráš, Roman - Škorík, Viktor - Polák, Jaroslav
    Damage Evolution in Thermomechanical Loading of Stainless Steel.
    21st European Conference on Fracture. Amsterdam: Elsevier, 2016, 3407–3414. Procedia Structural Integrity, 2. ISSN 2452-3216.
    [ECF21 - European Conference on Fracture /21./. Catania (IT), 20.06.2016-24.06.2016]
    Grant CEP: GA MŠMT LM2015069; GA MŠMT(CZ) LQ1601; GA ČR(CZ) GA13-23652S
    Institucionální podpora: RVO:68081723
    Klíčová slova: Thermomechanical fatigue * Sanicro 25 steel * Damage mechanism * FIB cutting * Localized oxidation-cracking
    Kód oboru RIV: JL - Únava materiálu a lomová mechanika

    Superaustenitic stainless steel Sanicro 25 has been subjected to in-phase and out-of-phase thermomechanical fatigue (TMF). Different amplitudes of mechanical strain and the changes of the temperature in the interval 250 to 700°C were applied to standard cylindrical specimens. Early fatigue damage has been studied using scanning electron microscopy combined with FIB cutting and EBSD imaging. TMF loading resulted first in developing thin oxide layer. In in-phase loading grain boundaries were preferentially oxidized and fatigue cracks developed by alternating oxidation and cracking. Fatigue cracks developed rapidly in oxidized grain boundaries and propagated intergranularly. During out-of-phase TMF loading the cracked oxide layer resulted in local oxidation and crack initiation. The crack grew transgranularly.
    Trvalý link: http://hdl.handle.net/11104/0264189

     
     