Water splitting and the band edge positions of TiO2

0458866 - ÚFCH JH 2017 RIV GB eng J - Článek v odborném periodiku
Deák, P. - Kullgren, J. - Aradi, B. - Frauenheim, T. - Kavan, Ladislav
Water splitting and the band edge positions of TiO2.
Electrochimica acta. Roč. 199, MAY 2016 (2016), s. 27-34. ISSN 0013-4686. E-ISSN 1873-3859
Grant CEP: GA ČR GA13-07724S
Grant ostatní: COST(XE) CM1104
Institucionální podpora: RVO:61388955
Klíčová slova: water splitting * rutile * anatase
Kód oboru RIV: CG - Elektrochemie
Impakt faktor: 4.798, rok: 2016

The possibility of splitting water by UV-light on a TiO2 electrode has created great interest in the material, however, it has been later questioned whether rutile can do the job at all without external bias. Anatase was suggested instead, but its efficiency is still a subject of debate. The problem is related to the position of the band edges, that is, of the Fermi-level (EF), with respect to the redox potentials of water. Here we present hybrid-functional calculations to align the band structures with the vacuum level, assuming the rutile (110) and anatase (101) surface being exposed to water. Our results show that both are capable of water splitting if no adsorbates other than molecular water are present. On a fully hydroxylated surface (i.e., H+ and OH- adsorption on undercoordinated surface oxygen and titanium atoms, respectively), EF is only ∼0.5 eV above the H+/H2 potential in case of anatase, and - depending on the level of reduction - roughly at, or below it for rutile. We also show, that the band edges (and EF) shift up if OH+ groups dominate the surface, increasing the driving force for water splitting. This is in line with the experience on titania reduced in hydrogen. Our results are further confirmed by calculating EF without the presence of water, and comparing it to work function measurements by photoelectron spectroscopy.