Photo- and radioluminescence of Dy.sup.3+./sup.-doped oxide glass with high-Gd.sub.2./sub.O.sub.3./sub. content

0458852 - FZÚ 2017 RIV DE eng J - Článek v odborném periodiku
Pattanaboonmee, N. - Lertloypanyachai, P. - Chewpraditkul, W. - Liu, W. - Chen, D. - Babin, Vladimir - Beitlerová, Alena - Nikl, Martin
Photo- and radioluminescence of Dy³⁺-doped oxide glass with high-Gd₂O₃ content.
Physica Status Solidi A. Roč. 213, č. 1 (2016), 133-138. ISSN 1862-6300. E-ISSN 1862-6319
Institucionální podpora: RVO:68378271
Klíčová slova: Dy³⁺ * energy transfer * photoluminescence * radioluminescence
Kód oboru RIV: BH - Optika, masery a lasery
Impakt faktor: 1.775, rok: 2016

Dy3+-doped oxide glass with 30 mol.% Gd2O3 content in the glass host was prepared by melt quenching under CO reducing atmosphere. The luminescence properties were investigated under UV and X-ray excitation. The 4F9/2-6HJ (J = 15/2, 13/2, 11/2, and 9/2) luminescence was observed with intense blue (484 nm; 4F9/2-6H15/2) and yellow (576 nm; 4F9/2-6H13/2) emissions. Energy transfer from Gd3+ to Dy3+ ions was confirmed by photoluminescence excitation and emission spectra as well as photoluminescence decay measurements. The integral scintillation efficiency of 11% of Bi4Ge3O12 scintillator was obtained.