Mass production of fluorescent nanodiamonds with a narrow emission intensity distribution

0458079 - ÚJF 2017 RIV US eng J - Článek v odborném periodiku
Štursa, Jan - Havlík, Jan - Petráková, Vladimíra - Gulka, Michal - Ráliš, Jan - Zach, Václav - Pulec, Zdeněk - Štěpán, Václav - Zargaleh, S. A. - Ledvina, Miroslav - Nesládek, M. - Treussart, F. - Cígler, Petr
Mass production of fluorescent nanodiamonds with a narrow emission intensity distribution.
Carbon. Roč. 96, JAN (2016), s. 812-818. ISSN 0008-6223. E-ISSN 1873-3891
Grant CEP: GA MŠMT(CZ) LM2011019; GA MZd(CZ) NV15-33094A
Institucionální podpora: RVO:61389005 ; RVO:61388963 ; RVO:68378271
Klíčová slova: nanodiamonds * luminescence * nitrogen-vacancy
Kód oboru RIV: BG - Jaderná, atomová a mol. fyzika, urychlovače; CH - Jaderná a kvantová chemie, fotochemie (UOCHB-X); BM - Fyzika pevných látek a magnetismus (FZU-D)
Impakt faktor: 6.337, rok: 2016

Fluorescent diamond nanocrystals are attracting increasing interest for a broad range of applications, from biolabeling and single particle tracking to nanoscale magnetic field sensing. Their fluorescence stems from nitrogen-vacancy color centers created within synthetic diamond nanoparticles by hightemperature annealing, which results in the association of pre-existing nitrogen impurities and vacancies generated by high-energy particle (electron, proton, or helium ion) beam irradiation. Up to now, diamond nanocrystals have been irradiated as dry powder in a container or deposited as a thin layer on a flat substrate, depending on the type and energy of the irradiating particles. However, these techniques suffer from intrinsic inhomogeneities: the fluence of particles may vary over the whole sample area, as well as the thickness and density of the nanodiamond layer. Here, we present an approach based on direct large-scale irradiation of nanodiamonds in aqueous colloidal solution by high-energy protons. This approach results in a larger fraction of fluorescent particles, with a more homogenous distribution of nitrogen-vacancy centers per particle and less severe lattice damages compared to dry powder irradiation.