Mechanical alloying of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic material of Permalloy type

0435587 - ÚFM 2015 RIV SK eng J - Článek v odborném periodiku
Hadraba, Hynek - Strečková, M. - Husák, Roman - Roupcová, Pavla
Mechanical alloying of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic material of Permalloy type.
Powder Metallurgy Progress. Roč. 14, č. 4 (2014), s. 208-214. ISSN 1335-8987
Grant CEP: GA ČR(CZ) GA14-25246S
Institucionální podpora: RVO:68081723
Klíčová slova: soft magnetic materials * Permalloy * mechanical alloying
Kód oboru RIV: JG - Hutnictví, kovové materiály

The paper describes preparation of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic alloy of Permalloy type by mechanical alloying from atomic powders. The powders were mechanically alloyed by high-energy ball milling in planetary mill under an air atmosphere. Comparing results from electron energy chemical analysis and X-ray diffraction analysis it was found that hardness of alloy corresponds to the chemical and phase homogeneity of composite powder. After 24 hours of milling the one phase homogenous composite powder was prepared having Vickers hardness about 750 HV1 and coercivity about 40 A.m-1. Further alloying led to powder grain size and crystallinite size refinement. This process was accompanied with defects amount increasing and thus with increasing of coercivity up to 120 A.m-1 after alloying for 120 hours.