Luminescence properties and scintillation response in Ce.sup.3+./sup.-doped Y.sub.2./sub.Gd.sub.1./sub.Al.sub.5-x./sub.Ga.sub.x./sub.O.sub.12./sub. (x = 2, 3, 4) single crystals
- 1.0432853 - FZÚ 2015 RIV US eng J - Článek v odborném periodiku
Chewpraditkul, Wa. - Pánek, D. - Brůža, P. - Chewpraditkul, W. - Wanarak, C. - Pattanaboonmee, N. - Babin, Vladimir - Bartosiewicz, Karol - Kamada, K. - Yoshikawa, A. - Nikl, Martin
Luminescence properties and scintillation response in Ce3+-doped Y2Gd1Al5-xGaxO12 (x = 2, 3, 4) single crystals.
Journal of Applied Physics. Roč. 116, č. 8 (2014), "083505-1"-"083505-7". ISSN 0021-8979. E-ISSN 1089-7550
Grant CEP: GA MŠMT(CZ) LH14266
GRANT EU: European Commission(XE) 316906 - F-CHROMA
Institucionální podpora: RVO:68378271
Klíčová slova: luminescence * scintillation * photoluminescence
Kód oboru RIV: BH - Optika, masery a lasery
Impakt faktor: 2.183, rok: 2014
The compositional dependence of luminescence properties and scintillation response were investigated in Ce3+-doped Y2Gd1Al5-xGaxO12 (x = 2, 3, 4) single crystals. The Gd3+ → Ce3+ energy transfer was evidenced by photoluminescence excitation spectra of Ce3+ emission. With increasing Ga content in the garnet host, the Ce3+ luminescence from the lowest 5d level (5d1) is shifted toward higher energy due to the decrease in the crystal field splitting of the 5d levels. Light yield (LY) and its dependence on the amplifier shaping time were measured under excitation with γ-rays. High LY value of 38 000 ph/MeV was obtained for a Y2Gd1Al3Ga2O12:Ce sample. Scintillation decay was measured with an extended dynamical and temporal scale under the nanosecond pulse soft X-ray excitation. The decrease of both LY value and relative contribution of slower decay component in the scintillation response was observed with increasing Ga content in the garnet host.