Carbonization of aniline oligomers to electrically polarizable particles and their use in electrorheology

0430195 - ÚMCH 2015 RIV NL eng J - Článek v odborném periodiku
Plachý, T. - Sedlačík, M. - Pavlínek, V. - Trchová, Miroslava - Morávková, Zuzana - Stejskal, Jaroslav
Carbonization of aniline oligomers to electrically polarizable particles and their use in electrorheology.
Chemical Engineering Journal. Roč. 256, 15 November (2014), s. 398-406. ISSN 1385-8947. E-ISSN 1873-3212
Grant CEP: GA ČR GAP205/12/0911; GA ČR(CZ) GA13-08944S
Institucionální podpora: RVO:61389013
Klíčová slova: aniline * aniline oligomers * carbonization
Kód oboru RIV: CD - Makromolekulární chemie
Impakt faktor: 4.321, rok: 2014

Aniline oligomers prepared via the oxidation of aniline under alkaline conditions at various concentrations of ammonia were carbonized at 650 °C in inert atmosphere. Subsequently, the prepared particles were mixed with silicone oil and the suspensions were used as electrorheological fluids. After the carbonization, when the higher amount of ammonia was present during the synthesis, the transition of morphology of the particles from microspheres to two-dimensional plates was observed. This transition led to a significant increase of viscosity of silicone-oil suspensions in the presence of external electric field, while their field-off viscosity remained nearly unchanged. Thus, the carbonization had the desired effect on the treated particles leading to extremely high electrorheological efficiency of the suspensions based on such particles. The highest electrorheological efficiency was achieved for the suspension based on carbonized particles prepared in 0.2 M ammonia. The dielectric spectroscopy was used as an evaluative tool of electrorheological performance of suspensions, and data correspond well with the obtained results from electrorheological experiments.