Thermal stability of nanocrystalline ε-Fe2O3
- 1.0429198 - ÚACH 2015 RIV HU eng J - Článek v odborném periodiku
Brázda, Petr - Večerníková, Eva - Pližingrová, Eva - Lančok, Adriana - Nižňanský, D.
Thermal stability of nanocrystalline ε-Fe2O3.
Journal of Thermal Analysis and Calorimetry. Roč. 117, č. 1 (2014), s. 85-91. ISSN 1388-6150. E-ISSN 1588-2926
Grant CEP: GA ČR GAP204/10/0035
Institucionální podpora: RVO:61388980
Klíčová slova: ε-Fe2O3 * Differential thermal analysis * Evolved gas analysis * Infrared spectroscopy * Thermogravimetry * X-ray powder diffraction
Kód oboru RIV: CA - Anorganická chemie
Impakt faktor: 2.042, rok: 2014
Thermal behavior of highly crystalline ε-Fe2O3 nanoparticles of different apparent crystallite sizes was characterized using thermogravimetry, differential thermal analysis, and analysis of evolved gas by mass spectrometry. Phase composition of the samples was monitored ex situ by X-ray powder diffraction. The results show that the thermal stability of this metastable iron oxide polymorph decreases with increasing particle size. For the particle diameter of 19(2) nm, the transformation temperature was equal to 794(5) °C, while for 28(2) nm only 755(10) °C. Surface of the nanoparticles contained adsorbed water and carbon dioxide. Elimination of these species proceeds in two steps. Water is removed at temperatures below 200 °C and CO2 in the temperature range between 200 and 450 °C.