Effect of air annealing on mechanical properties and structure of SiC.sub.x./sub.N.sub.y./sub. magnetron sputtered films
- 1.0427277 - FZÚ 2015 RIV CH eng J - Článek v odborném periodiku
Kulikovsky, V. - Čtvrtlík, Radim - Vorlíček, Vladimír - Železný, Vladimír - Boháč, Petr - Jastrabík, L.
Effect of air annealing on mechanical properties and structure of SiCxNy magnetron sputtered films.
Surface and Coatings Technology. Roč. 240, FEB (2014), s. 76-85. ISSN 0257-8972. E-ISSN 1879-3347
Grant CEP: GA ČR GAP108/12/1941; GA TA ČR TA03010743
Institucionální podpora: RVO:68378271
Klíčová slova: SiCN films * annealing * temperature stability * mechanical properties * structure
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 1.998, rok: 2014
Amorphous SiCxNy films (of 2.2–2.7 μm) were deposited on Si(111) substrates by reactive DC magnetron sputtering. The SiC target with small excess of carbon was sputtered at various nitrogen/argon gas flow ratios (0–0.48).The as-deposited films were additionally annealed at temperatures of 700, 900 and 1100 °C in the air during 30 min and at 900 °C in vacuum during 1 h. The depth profile of hardness and elastic modulus (nanoindentation), change of the film thickness, film composition and structure (Raman and Infrared spectroscopy) were investigated in dependence on annealing temperature and content of nitrogen. The hardness of the as-deposited films decreases with the growth of nitrogen/argon flow ratio.Air annealing at 1100 °C leads to intensive surface oxidation and formation of graphite-like structure in carbon clusters of inner layers.