Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer
- 1.0424542 - ÚMCH 2014 RIV GB eng J - Článek v odborném periodiku
Sevšek, U. - Brus, Jiří - Jeřábek, Karel - Krajnc, P.
Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer.
Polymer. Roč. 55, č. 1 (2014), s. 410-415. ISSN 0032-3861. E-ISSN 1873-2291
Grant CEP: GA ČR(CZ) GA13-29009S
Institucionální podpora: RVO:61389013 ; RVO:67985858
Klíčová slova: polyHIPE * hypercrosslinking * porous polymers
Kód oboru RIV: JI - Kompozitní materiály; CI - Průmyslová chemie a chemické inženýrství (UCHP-M)
Impakt faktor: 3.562, rok: 2014
Porous copolymers of styrene and divinylbenzene (DVB) were prepared by emulsion templating using high internal phase emulsions (HIPEs) as precursors for monoliths. The ratio of monomers was varied in order to obtain samples with different degrees of crosslinking and different amounts of unreacted vinyl groups originating from DVB. PolyHIPE monoliths were subjected to reswelling and treatment with a radical initiator. Significant enlargement of the amount of meso- and micropores in the material was found resulting in a substantial increase of BET surface area, up to 7.2 times compared to untreated polyHIPEs. The treated PolyHIPE monoliths retained the open macroporous morphology typical of polyHIPE materials. Solid state 13C NMR experiments were used to determine the amount of unreacted vinyl groups in polyHIPE samples, both before and after the hypercrosslinking treatment.