High-temperature long-service embrittlement of the R.A.F.M. EUROFER´97 steel

0332730 - ÚFM 2010 RIV IN eng A - Abstrakt
Hadraba, Hynek - Stratil, Luděk - Dlouhý, Ivo
High-temperature long-service embrittlement of the R.A.F.M. EUROFER´97 steel.
NMD-ATM 2009. Kolkata, 2009. s. 152.
[NMD-ATM 2009. 14.11.2009-17.11.2009, Kolkata]
Grant CEP: GA AV ČR IAA200410502; GA ČR GA106/08/1397
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: Eurofer97 * embrittlement * impact behaviour
Kód oboru RIV: JG - Hutnictví, kovové materiály

The ferritic-martensitic reduced activation steel Eurofer´97 is candidate structural material for in-vessel components of proposed fusion reactors. The embrittlement of the high-chromium ferritic-martensitic steels implies important limitation for use of these materials. The microstructure and fracture properties of the Eurofer´97 steel sheets of thickness 25 mm were investigated in as-received state and in state after long-time thermal ageing (550 °C/5.000 h/air). Detailed microstructure studies were carried out by means of optical, electron and quantitative electron microscopy in as-received state and in state after long-time thermal ageing. Mechanical properties were evaluated in both states by means of Charpy impact testing. The microstructure of the Eurofer´97 consisted of tempered martensite with M23C6 and MX precipitates. The isothermal ageing caused evident shift in tDBTT about +5 °C, no proofs of embrittlement were observed on fracture surfaces.