Plasma sprayed basalt/chromium oxide coatings

0319786 - ÚFP 2009 RIV US eng J - Článek v odborném periodiku
Ageorges, H. - Medarhri, Z. - Ctibor, Pavel - Fauchais, P.
Plasma sprayed basalt/chromium oxide coatings.
[Plazmové nástřiky směsi vytvořené z čedice a oxidu chromitého.]
High Temperature Materials and Processes. Roč. 11, č. 1 (2007), s. 71-82. ISSN 1093-3611. E-ISSN 1940-4360
Výzkumný záměr: CEZ:AV0Z20430508
Klíčová slova: Chromia, basalt * plasma spraying * microstructure * phase analysis
Kód oboru RIV: JH - Keramika, žáruvzdorné materiály a skla
Impakt faktor: 0.268, rok: 2007

Volcanic basalt and chromium oxide (Cr2O3) have been co-sprayed in air with a direct current (d.c.) plasma to obtain composite coatings. Both powders were simultaneously injected by two separated injectors. The following spray parameters: arc current, hydrogen vol. % and total plasma forming gas mass flow rate were optimized as well as injector positions. Different mass ratios of both components were used to achieve coatings. An uniform distribution of basalt among the Cr2O3 lamellae has been observed with SEM for all composite coatings. XRD showed that chromia became amorphous in the composite basalt/chromia coatings.

Čedič vulkanického původu a oxid chromitý (Cr2O3) byly společně podávány do plazmatu plazmatronu s plynovou stabilizací za účelem vytvoření kompozitních nástřiků. Hlavní parametry plazmatronu jako el. proud, obsah vodíku, celkový hmotový průtok plazmotvorného plynu a pozice podávacích injektorů byly optimalizovány pro danou kombinaci materiálů. Nástřiky záměrně obsahovaly různé podíly obou fází. Pomocí SEM bylo pozorováno rovnoměrné objemové rozložení obou složek. Rentgenografickou technikou bylo zjištěno, že oxid chromitý byl v nástřiku v amorfní podobě.