Fatigue Lifetime of ADI from Ultimate Tensile Strength to Permanent Fatigue Limit

0317577 - ÚFM 2009 RIV UA eng J - Článek v odborném periodiku
Zapletal, J. - Věchet, S. - Kohout, J. - Obrtlík, Karel
Fatigue Lifetime of ADI from Ultimate Tensile Strength to Permanent Fatigue Limit.
[Únavová životnost ADI od pevnosti v tahu po mez únavy.]
Problemy pročnosti (Strength of Materials). -, č. 1 (2008), s. 40-43. ISSN 0556-171X.
[MSMF /5./. Brno, 27.06.2007-29.06.2007]
Grant CEP: GA ČR GA106/03/1265
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: austempered ductile iron * fatigue behaviour * S N curve
Kód oboru RIV: JL - Únava materiálu a lomová mechanika

S-N curve of ADI (austempered ductile iron) was obtained in the range of lifetime including low cycle fatigue domain and high cycle fatigue domain up to 10 million cycles. UTS is used as a limiting value of the curve. Symmetric push-pull fatigue and tensile tests were performed at room temperature on nodular cast iron .

Wöhlerova křivka životnosti litiny s kuličkovým grafitem byla získána v širokém rozmezí od nízkcyklové únavy až po 10 milionů cyklů. Mez pevnosti je použita jako limitní bod křivky. Litina s kuličkovým grafitem byla zatěžována v symetrickém cyklu s řízenou silou a tahová zkouška byla provedena při pokojkové teplotě.