Crystallite size and sinterability of tungsten

0315382 - ÚFP 2009 RIV CZ eng K - Konferenční příspěvek (tuzemská konf.)
Brožek, Vlastimil - Maixner, J. - Domlátil, J. - Janča, J. - Eliáš, M.
Crystallite size and sinterability of tungsten.
[Krystalinita a slinovatelnost wolframu.]
Proceedings of the 18th Joint seminar Development of materials science in research and education. Praha: Czechoslovak association for crystal growth, 2008 - (Nitsch, K.; Rodová, M.), s. 12-13. ISBN 978-80-254-0864-3.
[Joint seminar Development of materials science in research and education/18th./. Hnanice (CZ), 02.09.2008-05.09.2008]
Výzkumný záměr: CEZ:AV0Z20430508
Klíčová slova: Sintering activity * tungsten * plasmachemical reduction * hydrogen plasma * crystallite size
Kód oboru RIV: BL - Fyzika plazmatu a výboje v plynech

Sintering activity of tungsten powders of various origin was tested by modified technique according Agte. The size of crystallites calculated according to Scherrer formula corresponds with density values detected by Mercury porosimetry. Tungsten poder obtained by reduction of tungstates in hydrogen plasma can be recovered to 93 % of theoretical density at the temperature 1350°C. Next increase of the density needs simultaneous application of high pressure. By the BELT technique 95 % density was reached, by plasma spheroidization up to 98 %.

Slinovací aktivita wolframových prášků různé provenience byla testována modifikovanou metodou dle Agteho.Velikost krystalitů, vypočtená ze |Scherrerovy rovnice, koresponduje s hodnotami hustot, měřenými rtutovou porozimetrií. Wolframový prášek získaný redukcí wolframanů ve vodíkovém plazmatu lze konsolidovat na 93 % teoretické hustoty již při teplotě 1350°C, další zvyšování hustoty vyžaduje současnou aplikaci vysokých tlaků. Metodou BELT bylo dosaženo hustoty 95 %, u plazmové sferoidizace až 98 %.