Constraint Effects at Brittle Fracture Initiation in a Cast Ferritic Steel

  1. 1.
    0178125 - UFM-A 20033145 RIV GB eng J - Článek v odborném periodiku
    Dlouhý, Ivo - Chlup, Zdeněk - Kozák, Vladislav
    Constraint Effects at Brittle Fracture Initiation in a Cast Ferritic Steel.
    Engineering Fracture Mechanics. č. 71 (2004), s. 873-883. ISSN 0013-7944. E-ISSN 1873-7315
    Grant CEP: GA AV ČR IAA2041003
    Výzkumný záměr: CEZ:AV0Z2041904
    Klíčová slova: Cast ferritic steel * transition behaviour * fracture toughness
    Kód oboru RIV: JL - Únava materiálu a lomová mechanika
    Impakt faktor: 1.299, rok: 2004
    www.sciencedirect.com

    The fracture resistance of a cast low carbon manganese ferritic steel intended for containers for spent nuclear fuel has been analysed by combining several approaches.Based on data from three-point bend specimens with shallow and deep cracks the e .ect of crack tip constraint at brittle fracture initiation has been followed.Q -parameter was used for the constraint quanti .cation.The crack length e .ect on the fracture toughness - temperature diagram has been analysed and peculiarities of fracture behaviour in the lower shelf region have been explained.The role of cleavage fracture stress in brittle fracture initiation under the in .uence of crack tip constraint has been analysed.