Interdiffusion in ternary Ni3Al/Ni3Al-X diffusion couples with X = Cr, Fe, Nb and Ti

  1. 1.
    0178018 - UFM-A 20033033 RIV GB eng J - Článek v odborném periodiku
    Čermák, Jiří - Gazda, Aleš - Rothová, Věra
    Interdiffusion in ternary Ni3Al/Ni3Al-X diffusion couples with X = Cr, Fe, Nb and Ti.
    Intermetallics. Roč. 11, č. 9 (2003), s. 939-946. ISSN 0966-9795. E-ISSN 1879-0216
    Grant CEP: GA AV ČR IBS2041105; GA ČR GA106/00/0173
    Výzkumný záměr: CEZ:AV0Z2041904
    Klíčová slova: interdiffusion * Ni3Al * intermetallics
    Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
    Impakt faktor: 1.619, rok: 2003

    The gamma' single phase interdiffusion in selected pseudo-binary sections of the Ni3Al-X (X = Cr, Fe, Nb and Ti) ternary alloys was studied in temperature interval 1173-1533 K in order to assess the influence of the site-preference of components upon their diffusion rate. It was observed that (a) Higher fraction of Cr or Fe on Al sublattice leads to lower values of D ((Ni))(XX). (b) Both Ti and Nb, preferring strongly the Al sublattice, show significantly lower interdiffusion coefficients than Fe and Cr. (c) The equation D-XX((Ni)) = D-AlAl((Ni)) holds for Ti and Nb, whereas the relation D-XX((Ni)) > D-AlAl((Ni)) is valid for Cr and Fe. (d) Activation enthalpy of Q(ii)((i)) shows a systematic decrease with increasing valence electron number of the alloying element i. (e) Nb shows a transient behavior Q - it has low values of diffusion coefficient compared to its site occupation but also a low activation energy.