Young`s modulus of ceramic matrix composites with polysiloxane based matrix at elevated temperatures

0106026 - USMH-B 20040039 RIV NL eng J - Článek v odborném periodiku
Černý, Martin - Glogar, Petr
Young`s modulus of ceramic matrix composites with polysiloxane based matrix at elevated temperatures.
[Modul pružnosti kompozitů s keramickou matricí odvozenou od polysiloxanu při zvýšených teplotách.]
Journal of Materials Science. Roč. 39, č. 6 (2004), s. 2239-2242. ISSN 0022-2461. E-ISSN 1573-4803
Grant CEP: GA ČR GA106/02/0177; GA ČR GP106/02/P025
Výzkumný záměr: CEZ:AV0Z3046908
Klíčová slova: composite material * Young`s modulus * high temperature
Kód oboru RIV: JI - Kompozitní materiály
Impakt faktor: 0.864, rok: 2004

The Young`s modulus of unidirectional composites with matrix derived from cured polysiloxanes and reinforced with SiC or alumina fibres was measured at temperatures up to 1300°C. At 1200 and 1300°C a substantial deterioration of the Young`s modulus occurs, which falls to 75-80% of its room-temperature value for Nicalon reinforced composites and to 65-70% for Nextel reinforced composites.

Studie se zabývá měřením Youngova modulu jednosměrných kompozitů s matricí na bázi pyrolyzovaných polysiloxanových pryskyřic vyztužených buď SiC nebo korundovými vlákny při teplotách do 1300°C. V rozmezí teplot 1200 až 1300°C dochází ke snížení Youngova modulu na 75-80% hodnoty při pokojové teplotě u Nikalonem vyztužených kompozitů a 65-70 u Nextelem vyztužených kompozitů.
Trvalý link: http://hdl.handle.net/11104/0013209