Effect of electrical field on dipoles in polymer composites

  1. 1.
    0101839 - UJF-V 20043006 RIV US eng J - Článek v odborném periodiku
    Švorčík, V. - Gardacova, R. - Rybka, V. - Hnatowicz, Vladimír - Červená, Jarmila - Plesek, J.
    Effect of electrical field on dipoles in polymer composites.
    [Vliv elektrického pole na dipóly v polymerních kompozitech.]
    Journal of Applied Polymer Science. Roč. 91, č. 1 (2004), s. 40-45. ISSN 0021-8995. E-ISSN 1097-4628
    Grant CEP: GA ČR GA102/01/1324
    Výzkumný záměr: CEZ:AV0Z1048901
    Klíčová slova: poly(methyl methacrylate) * polystyrene * composites
    Kód oboru RIV: BG - Jaderná, atomová a mol. fyzika, urychlovače
    Impakt faktor: 1.021, rok: 2004

    Orientation of two bipolar compounds embedded in polymer composites was studied. Poly(methyl methacrylate) (PMMA) dissolved in acetone was doped with a cobaltborane derivative of 1,2-dimethylimidazole and polystyrene (PS) dissolved in toluene was doped with the 3-(1,2-dimethyl imidazole)-borane. To orient the dipoles, the composites were exposed to external electrical field: PMMA composite at the temperature of glass transition (T-g) and PS composite during evaporation of the toluene solvent. The degree of dipole orientation was estimated by the change in relative permittivity (epsilon) of the resulting composite film. The dependence of the epsilon on the temperature, frequency, voltage, and dipole concentration was studied. It was found that the dipole's distribution in the composite film was not homogenous. At the T-g, the dipoles in PMMA became oriented by external direct electrical field and the orientation was conserved after cooling to lower temperatures. In a PS-based composite, the significant permittivity increase was observed already at low-dopant concentrations. The dipole orientation achieved during solvent evaporation was also permanent and the composite permittivity was an increasing function of the film thickness.

    Byla studována orientace dvou bipolárních sloučenin vložených v polymerním kompozitu. Stupeň dipólové orientace byl určen změnami relativní permitivity výsledného kompozitního filmu. Byla studována závislost na teplotě, frekvenci, napětí a koncentraci dipólů.