Hydrogen diffusion in hydrogenated Mg and Mg-Mg2Ni eutectic alloy

0091255 - ÚFM 2008 RIV SK eng J - Článek v odborném periodiku
Čermák, Jiří - Král, Lubomír - Stloukal, Ivo
Hydrogen diffusion in hydrogenated Mg and Mg-Mg2Ni eutectic alloy.
[Difúze vodíku v hydrogenovaném Mg a v eutektické slitině Mg-Mg2Ni.]
Kovové materiály. Roč. 45, č. 6 (2007), s. 305-312. ISSN 0023-432X. E-ISSN 1338-4252
Grant CEP: GA ČR GA106/07/0010
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: magnesium intermetallic phases * hydrogen diffusion * hydrogen storage
Kód oboru RIV: BJ - Termodynamika
Impakt faktor: 1.345, rok: 2007
http://www.kovmat.sav.sk/full.php?rr=45&cc=6&ss=305

Time dependence of total amount of hydrogen desorbed from hydrogen-charged Mg and eutectic Mg-Mg2Ni (23.5 wt.% Ni) alloy was measured at temperatures from interval 552–723 K. Experiments were carried out well below the equilibrium pressure, where these hydrides – perspective as solid hydrogen storage media – are unstable and the desorption process is controlled mainly by diffusion of hydrogen in respective hydride (MgH2 and/or Mg2NiH4). Hydrogen diffusion coefficients were evaluated from desorption curves and hydrogen diffusion coefficient along interphase boundary MgH2/Mg2NiH4 was estimated from results obtained with the eutectic alloy.

V teplotním intervalu 552-723 K byla studována časová závislost celkového množství vodíku desorbovaného z hydrogenovaného Mg a eutektické slitiny Mg-Mg2Ni (23,5 hm.% Ni). Experimenty byly prováděny hluboko pod rovnovážným tlakem, kde jsou tyto hydridy - perspektivní jako pevná média pro uchovávání vodíku - nestabilní a desorpční proces je hlavně řízen difúzí vodíku v příslušném hydridu (MgH2 a/nebo Mg2NiH4). Difúzní koeficienty vodíku byly vyhodnoceny z desorpčních křivek a ddifúzní koeficient vodíku podél mezifázové hranice MgH2/Mg2NiH4 byl odhadnut z výsledků získaných na eutektické slitině.