The effect of carbon on the structure of Fe-40Al-xC (at.%)

0091034 - ÚFM 2008 RIV SK eng J - Článek v odborném periodiku
Vodičková, V. - Kratochvíl, P. - Dobeš, Ferdinand
The effect of carbon on the structure of Fe-40Al-xC (at.%).
[Vliv uhlíku na strukturu slitiny Fe-40Al-xC (at.%).]
Kovové materiály. Roč. 45, č. 3 (2007), s. 153-158. ISSN 0023-432X. E-ISSN 1338-4252
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: iron aluminide (Fe-Al type) * phase composition
Kód oboru RIV: JG - Hutnictví, kovové materiály
Impakt faktor: 1.345, rok: 2007

The phase composition of Fe-40Al-xC (at.%) alloys depends on the content of C. The part of the quasibinary phase diagram is determined using light optical microscopy (LOM), Vickers hardness measurements (HV) and X-rays diffraction (XRD). The composition of the tested alloys approaches in succesive steps Pyroferal alloy used in the fifties to replace the high chromium and nickel alloyed cast iron. The structural data are compared with those resulting from quasibinary Fe40Al-xC as well as ternary Fe-Al-C phase diagrams.

Fázové složení slitin Fe-40Al-xC (at.%) závisí na obsahu uhlíku. Část kvazibinárního fázového diagramu byla určována pomocí světelné mikroskopie, měření Vickersovy tvrdosti a rentgenovské difrakce. Složení zkoušených slitin se postupnými kroky blíží ke slitině Pyroferal, používané v padesátých letech jako náhrada chromových a niklových slitin na bázi železa. Mikrostrukturní údaje jsou porovnávány s údaji z kvazibinárního diagramu Fe40Al-xC a z ternárního diagramu Fe-Al-C.