Sensitivity of microstructure fibers to gaseous oxygen

0044011 - ÚFE 2007 TN eng A - Abstrakt
Matějec, Vlastimil - Mrázek, Jan - Hayer, Miloš - Podrazký, Ondřej - Kaňka, Jiří - Kašík, Ivan
Sensitivity of microstructure fibers to gaseous oxygen.
[Citlivost mikrostrukturních vláken k plynému kyslíku.]
MADICA 2006. Recueil des Résumes. Monastir: [Université de Monastir], 2006. s. 94--.
[Journees Maghreb-Europe sur les Materiaux et Leurs Applications aux Dispositifs et Capteurs MADICA 2006 /5./. 30.10.2006-01.11.2006, Mahdia]
Grant CEP: GA ČR(CZ) GA102/05/0956
Výzkumný záměr: CEZ:AV0Z20670512
Klíčová slova: detection * fibre optic sensors * oxygen * aerogels
Kód oboru RIV: JB - Senzory, čidla, měření a regulace

Different types of microstructure fibers were fabricated from input stacks composed of silica tubes and rods. The sensitivity of these fibers to oxygen was induced by the application xerogel detection layers containing Ru-complex , tris (1,10-phenantroline) ruthenium chloride hydrate. The sensitivity was determined from changes of fluorescence of the complex caused by oxygen . In experiments the fibers were side excited at about 480 nm and fluorescence at about 590 nm was detected.

Různé typy mikrostrukturních vláken byly připraveny z výchozích svazků složených z křemenných trubic a tyček. Citlivost těchto vláken ke kyslíku byla vyvolána nanesením detekčních xerogelových vrstev s Ru komplexem, tris(1,10-phenantroline)ruthenium chloride hydratem. Citlivost byla určena ze změn fluorescence komplexu způsobených kyslíkem. V experimentech byla vlákna stranově excitována při 480 nm a fluorescence při 590 nm byla detekována.
Trvalý link: http://hdl.handle.net/11104/0136888