Fatigue notch sensitivity of ultrafine-grained copper

0024111 - ÚFM 2011 RIV GB eng J - Článek v odborném periodiku
Lukáš, Petr - Kunz, Ludvík - Svoboda, Milan
Fatigue notch sensitivity of ultrafine-grained copper.
[Únavová vrubová citlivost ultrajemnozenné mědi.]
Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. Roč. 391, - (2005), s. 337-341. ISSN 0921-5093. E-ISSN 1873-4936
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: Ultrafine-grained copper * Fatigue notch sensitivity * Stability of grain structure
Kód oboru RIV: BM - Fyzika pevných látek a magnetismus
Impakt faktor: 1.347, rok: 2005

Fatigue notch sensitivity of ultrafine-grained (UFG) copper of purity 99.9% produced by equal-channel angular pressing (ECAP) was determined on cylindrical specimens with circumferential notches of different radii and compared with the notch sensitivity of conventional copper. Notch sensitivity of UFG copper is higher than that of its conventional counterpart. Electron back scattering diffraction (EBSD) technique showed that the UFG copper of purity 99.9% is not prone to grain coarsening during cycling. The grain structure within plastic zone around the cracks was found to differ substantially from that outside the plastic zone: the grains were markedly elongated, but their size was preserved.

Únavová vrubová citlivost ultrajemnozrnné (UFG) mědi čistoty 99.9% připravené metodou ECAP byla stanovena na válcových vzorcích s obvodovými vruby o různých poloměrech; výsledky byly porovnány s vrubovou citlivosti konvenční mědi. Vrubová citlivost je vyšší v případě UFG mědi. EBSD technika v elektronovém mikroskopu ukázala, že UFG měď čistoty 99.9% není náchylná ke zhrubnutí zrna při cyklické deformaci. Struktura zrn v plastické zóně kolem únavových trhlin se podstatně liší od struktury vně plastické zóny; zrna jsou zřetelně protažena, avšak jejich velikost zůstává zachována.
Trvalý link: http://hdl.handle.net/11104/0114707