Silver-doped hydroxyapatite coatings deposited by suspension plasma spraying

SYSNO ASEP	0498201
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Silver-doped hydroxyapatite coatings deposited by suspension plasma spraying
Tvůrce(i)	Čížek, Jan (UFP-V)_ORCID Brožek, Vlastimil (UFP-V)_RID Chráska, Tomáš (UFP-V)_{RID, ORCID} Lukáč, František (UFP-V)_ORCID Medřický, Jan (UFP-V)_RID Mušálek, Radek (UFP-V)_{RID, ORCID} Tesař, Tomáš (UFP-V)_ORCID Šiška, Filip (UFM-A)_{RID, ORCID} Antos, Z. (CZ) Čupera, J. (CZ) Matejková, M. (CZ) Spotz, Z. (CZ) Houdková, Š. (CZ) Kverka, Miloslav (MBU-M)_{RID, ORCID}
Celkový počet autorů	14
Zdroj.dok.	Journal of Thermal Spray Technology. - : Springer - ISSN 1059-9630 Roč. 27, č. 8 (2018), s. 1333-1343
Poč.str.	11 s.
Jazyk dok.	eng - angličtina
Země vyd.	US - Spojené státy americké
Klíč. slova	antibacterial property ; HA ; hybrid water-stabilized plasma ; liquid feedstock ; Silver compounds
Vědní obor RIV	JK - Koroze a povrchové úpravy materiálů
Obor OECD	Coating and films
Vědní obor RIV – spolupráce	Ústav fyziky materiálu - Koroze a povrchové úpravy materiálů Mikrobiologický ústav - Mikrobiologie, virologie
CEP	GB14-36566G GA ČR - Grantová agentura ČR
Institucionální podpora	UFP-V - RVO:61389021 ; UFM-A - RVO:68081723 ; MBU-M - RVO:61388971
UT WOS	000452893200009
EID SCOPUS	85055292484
DOI	10.1007/s11666-018-0767-2
Anotace	Pure hydroxyapatite suspension was produced by wet chemical synthesis. Using a hybrid water-stabilized torch, a series of HA coatings were produced on SS304 and Ti6Al4V substrates and their properties were characterized by SEM, EDX and XRD techniques. After deposition, the amorphous phase content reached 6-10% and the coatings retained 75-82% of crystalline HA phase. Their thickness reached 145 μm. To understand the wear behavior of the coatings, pin-on-disc tribology evaluation was performed. Additionally, a set of HA coatings was prepared with pure metallic Ag content. This formed by in situ chemical decomposition of AgNO3 added into the HA suspension. The Ag was dispersed evenly within the coatings in the form of submicron-sized particles situated predominantly along the HA splats boundaries with a total Ag content of 8 wt.%. Given the antibacterial properties of Ag, such result presents a promising step forward in the hard tissue replacement research.
Pracoviště	Ústav fyziky plazmatu
Kontakt	Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975
Rok sběru	2019
Elektronická adresa	https://link.springer.com/article/10.1007/s11666-018-0767-2