Nanomechanical testing of an a-C:N nanolayer prepared by ion beam assisted deposition on Ti.sub.6./sub.Al.sub.4./sub.V alloy
- 1.
SYSNO ASEP 0486538 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Nanomechanical testing of an a-C:N nanolayer prepared by ion beam assisted deposition on Ti6Al4V alloy Tvůrce(i) Vlčák, P. (CZ)
Šepitka, J. (CZ)
Horaždovský, T. (CZ)
Jirka, Ivan (UFCH-W) RID, ORCID
Gregora, Ivan (FZU-D) RID, ORCID
Němec, M. (CZ)Celkový počet autorů 6 Zdroj.dok. NANOCON 2015: 7th International Conference on Nanomaterials - Research and Application, Conference Proceedings. - Ostrava : TANGER, spol. s r.o., 2015 - ISBN 978-80-87294-63-5 Rozsah stran s. 68-72 Poč.str. 5 s. Forma vydání Tištěná - P Akce NANOCON 2015. International Conference /7./ Datum konání 14.10.2015 - 16.10.2015 Místo konání Brno Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova carbon-based materials ; hardness ; ion beam assisted deposition ; a-C:N nanolayer Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) Institucionální podpora FZU-D - RVO:68378271 ; UFCH-W - RVO:61388955 UT WOS 000374708800010 EID SCOPUS 84962875087 Anotace We applied ion beam assisted deposition for preparing a-C:N nanolayers on Ti6Al4V alloy. A Hysitron TI 950 TriboIndenter (TM) nanomechanical test instrument was used to assess the depth profiles of the mechanical properties on modified titanium substrates. Two methods were employed : a) quasistatic partial unload, and b) dynamic Continuous Measurement of X (CMX). The average nanoindentation hardness increased from HIT similar to 5GPa for a reference sample to HIT similar to 8.6 GPa for a sample coated by an a-C nanolayer, and to HIT similar to 11.5 GPa for a sample coated by an a-C:N nanolayer. The average storage modulus of the sample coated by a-C:N increased from E' similar to 130 GPa (reference sample) to E' similar to 155 GPa. The storage modulus of the sample coated by the a-C nanolayer was less than the storage modulus of the titanium substrate. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2018
Počet záznamů: 1