Ultrafast beam dump materials and mirror coatings tested with the ELI beamlines LIDT test station
- 1.
SYSNO ASEP 0470422 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Ultrafast beam dump materials and mirror coatings tested with the ELI beamlines LIDT test station Tvůrce(i) Ďurák, Michal (FZU-D) RID
Kramer, Daniel (FZU-D) RID
Velpula, Praveen K. (FZU-D)
Cupal, Josef (FZU-D) ORCID
Medřík, Tomáš (FZU-D)
Hřebíček, Jan (FZU-D)
Golasowski, Jiří (FZU-D)
Peceli, Davorin (FZU-D) RID
Fekete, Ladislav (FZU-D) RID, ORCID
Štepán, V. (CZ)
Kozlová, Michaela (FZU-D) RID, ORCID
Rus, Bedřich (FZU-D) ORCIDČíslo článku 96321B Zdroj.dok. Laser-Induced Damage in Optical Materials. - Bellingham : SPIE, 2015 / Exarhos G.J. ; Gruzdev V.E. ; Menapace J.A. ; Ristau D. ; Soileau M.J. - ISSN 0277-786X - ISBN 978-162841832-3 Rozsah stran s. 1-12 Poč.str. 12 s. Forma vydání Tištěná - P Akce Annual Laser Damage Symposium on Optical Materials for High-Power Lasers /47./ Datum konání 27.09.2015 - 30.09.2015 Místo konání Boulder Země US - Spojené státy americké Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova laser damage ; S-on-1 ; femtosecond ; ultrafast mirror ; absorptive coating ; vacuum Vědní obor RIV BH - Optika, masery a lasery CEP ED1.1.00/02.0061 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora FZU-D - RVO:68378271 UT WOS 000373355700031 EID SCOPUS 84964941471 DOI 10.1117/12.2194970 Anotace The ELI Beamlines project will deliver ultrafast laser pulses with peak powers up to 10PW available every minute and PW class beams at 10Hz complemented by a 10TW 1kHz beamline. To properly determine damage thresholds of involved optical components in conditions similar to the operational environment and with expected laser parameters, a high vacuum LIDT test station was constructed at PALS facility. Our study presents results of ISO based S-on-1 and R on 1 tests in femtosecond regime (50fs, 800nm, 10Hz/1kHz) performed on two different types of coatings: a) high-absorption black coatings with low outgassing rates, intended for use as a beam dump surface; and b) high-reflectivity, low-dispersion 45° AOI ultrafast mirror coatings. Testing of absorptive coatings was accompanied with QMS residual gas analysis to verify, that high intensity laser radiation approaching the damage threshold does not increase concentration of volatile organic compounds in the vacuum chamber. In case of HR mirror coatings, we also investigate the effect of cleaning on LIDT value, comparing characteristic S-on-1 curves of given sample with values obtained after 12h immersion in ethanol-water solution. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2017