Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region

  1. 1.
    0361095 - UFM-A 2012 RIV CH eng J - Článek v odborném periodiku
    Lukáš, Petr - Kunz, Ludvík - Navrátilová, Lucie - Bokůvka, O.
    Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region.
    Materials Science and Engineering A-Structural materials. Roč. 528, - (2011), s. 7036-7040 ISSN 0921-5093
    Grant CEP: GA ČR GAP108/10/2001
    Výzkumný záměr: CEZ:AV0Z20410507
    Klíčová slova: ultrafine-grained microstructure * ultrasonic fatigue * crack initiation * copper
    Kód oboru RIV: JL - Únava materiálu a lomová mechanika
    Impakt faktor: 2.003, rok: 2011

    Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 108 to 2x1010 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.