Niobium-Doped Titania Nanoparticles: Synthesis and Assembly into Mesoporous Films and Electrical Conductivity

  1. 1.
    0348369 - UFCH-W 2011 RIV US eng J - Článek v odborném periodiku
    Liu, Y. - Szeifert, J. M. - Feckl, J. M. - Mandlmeier, B. - Rathouský, Jiří - Heyden, O. - Fattakhova-Rohlfing, D. - Bein, T.
    Niobium-Doped Titania Nanoparticles: Synthesis and Assembly into Mesoporous Films and Electrical Conductivity.
    ACS Nano. Roč. 4, č. 9 (2010), s. 5373-5381 ISSN 1936-0851
    Grant CEP: GA ČR GA104/08/0435
    Výzkumný záměr: CEZ:AV0Z40400503
    Klíčová slova: nanoparticle synthesis * nanoparticle self-assembly * conducting
    Kód oboru RIV: CF - Fyzikální chemie a teoretická chemie
    Impakt faktor: 9.855, rok: 2010

    Crystalline niobium-doped titania nanoparticles were synthesized via solvothermal procedures using tert-butyl alcohol as a novel reaction medium, and their assembly into mesoporous films was investigated. The solvothermal procedure enables the preparation of crystalline doped and undoped nonagglomerated titania nanoparticles, whose size can be controlled from 4 to 15 nm by changing the reaction temperature and time. The anatase lattice of these particles can incorporate more than 20 mol % of Nb ions. The nanoparticles can be easily dispersed at high concentrations in THF to form stable colloidal suspensions and can be assembled into uniform porous mesostructures directed by the commercial Pluronic block copolymer F127. The resulting mesoporous films show a regular mesostructure with ad spacing of about 17 nm, a uniform pore size of about 10 nm with crystalline walls, a high porosity of 43%, and a large surface area of 190 m(2) cm(-3).