2022 Volume 63 Issue 11 Pages 1590-1596
CeNF/Al-based composites were prepared using CeNFs collected by a non-woven aluminum filter, followed by hot extrusion to obtain plates. Gel-like CeNFs were collected by an aluminum non-woven filter and compacted by a warm press to obtain a compressed form with a lighter specific density than pure aluminum. The compressed forms were hot extruded to fabricate bars and plates. Both bars and plates were observed in the macro-and microstructural morphology and XRD measurements. They were not significantly carbonized to graphite only, which was inferred to be present as CeNF under the present experimental conditions. Microstructural observations show that CeNFs are aggregated and present in the pores/cracks between the Al filters in the compressed forms. Al filters and CeNF aggregates were more finely mixed when the material was fabricated into hot extruded plates with a higher extrusion ratio. The maximum tensile strength of the CeNF/Al composite extruded plate was about 1.5 times higher than pure aluminum. In addition, the extruded plates could be cold-rolled by about 30%, and the maximum tensile strength of the extruded sheets was found to be about twice that of pure aluminum.