Wear characteristics and defects analysis of friction stir welded joint of aluminium alloy 6061-t6
- 1.
SYSNO ASEP 0455231 Document Type J - Journal Article R&D Document Type Journal Article Subsidiary J Článek ve WOS Title Wear characteristics and defects analysis of friction stir welded joint of aluminium alloy 6061-t6 Author(s) Kumar, R. (IN)
Chattopadhyaya, S. (IN)
Hloch, Sergej (UGN-S) RID, SAI, ORCID
Krolczyk, G. (PL)
Legutko, S. (PL)Number of authors 5 Source Title Eksploatacja i Niezawodnosc-Maintenance and Reliability - ISSN 1507-2711
Roč. 18, č. 1 (2016), s. 128-135Number of pages 8 s. Publication form Online - E Language eng - English Country PL - Poland Keywords Friction stir welding (FSW) ; grinding machine ; Field Emission Scanning Electron Microscope (FESEM) Subject RIV JQ - Machines ; Tools Institutional support UGN-S - RVO:68145535 UT WOS 000367163800017 EID SCOPUS 2-s2.0-84951311103 DOI https://doi.org/10.17531/ein.2016.1.17 Annotation This paper deals with the wear characteristics and defects developed during friction stir welding at different process parameter of aluminium alloy (AA) 6061-T6 having thickness 6 mm. Four welded samples are prepared with rotational speed 500 rpm, 710 rpm, 1000 rpm and with welding speed of 25 mm/min & 40 mm/min. Welded samples and base material are put in wear condition under grinding machine for 120 s. Material removal is measure by taking the difference of weight before and after wear. Different types of defects and fracture are observed on the wear surface. These defects and fractures are analysed under field emission scanning electron microscope (FESEM). It is concluded that material removal from welded sample is less compared to base metal, hence wear resistance increases after friction stir welding. Workplace Institute of Geonics Contact Lucie Gurková, lucie.gurkova@ugn.cas.cz, Tel.: 596 979 354 Year of Publishing 2016 Electronic address http://www.ein.org.pl/2016-01-17
Number of the records: 1