LOW CYCLE FATIGUE BEHAVIOR AND FATIGUE CRACK INITIATION IN MAR-M247 AT 700 °C

  1. SYS0491917
    LBL
      
    01000a^^22220027750^450
    005
      
    20240103220309.7
    014
      
    $a 85043373713 $2 SCOPUS
    014
      
    $a 000434346900255 $2 WOS
    017
      
    $2 DOI
    100
      
    $a 20180802d m y slo 03 ba
    101
      
    $a eng $d eng
    102
      
    $a CZ
    200
    1-
    $a LOW CYCLE FATIGUE BEHAVIOR AND FATIGUE CRACK INITIATION IN MAR-M247 AT 700 °C
    215
      
    $a 7 s. $c C
    463
    -1
    $1 010 $a 978-80-87294-79-6 $1 200 1 $a METAL 2017 - 26th International Conference on Metallurgy and Materials, Conference Proceedings $v S. 1580-1586 $1 210 $a Ostrava $c Tanger $d 2017
    610
      
    $a Nickel-based superalloy
    610
      
    $a cyclic stress-strain curve
    610
      
    $a Fatigue life
    610
      
    $a fatigue crack initiation
    610
      
    $a focus ion beam
    700
    -1
    $3 cav_un_auth*0309532 $4 070 $a Šulák $b Ivo $p UFM-A $i Nízkocyklová únava $j Low cycle fatigue $w Low Cycle Fatigue Group $y CZ $z K $T Ústav fyziky materiálů AV ČR, v. v. i.
    701
    -1
    $3 cav_un_auth*0101304 $4 070 $a Obrtlík $b Karel $p UFM-A $i Nízkocyklová únava $j Low cycle fatigue $w Low Cycle Fatigue Group $T Ústav fyziky materiálů AV ČR, v. v. i.
    701
    -1
    $3 cav_un_auth*0220963 $4 070 $a Hrbáček $b K. $y CZ
Number of the records: 1  