High cycle fatigue of nickel-based superalloy MAR-M 247 at high temperatures
SYS 0435146 LBL 02574^^^^^2200433^^^450 005 20240103205041.8 014 $a 84904421075 $2 SCOPUS 014 $a 000396733300060 $2 WOS 017 70
$a 10.1016/j.proeng.2014.06.273 $2 DOI 100 $a 20141124d m y slo 03 ba 101 0-
$a eng $d eng 102 $a NL 200 1-
$a High cycle fatigue of nickel-based superalloy MAR-M 247 at high temperatures 215 $a 4 s. $c E 300 $a doplnit UT WOS 463 -1
$1 001 cav_un_epca*0432845 $1 011 $a 1877-7058 $1 200 1 $a XVII International Colloquium on Mechanical Fatigue of Metals (ICMFM17) $v S. 329-332 $1 210 $a Amsterdam $c Elsevier $d 2014 $1 225 $a Procedia Engineering $v 74 $1 702 1 $a Gulagliano $b M. $4 340 $1 702 1 $a Vergani $b L. $4 340 610 0-
$a High cycle fatigue 610 0-
$a Superalloy 610 0-
$a MAR-M 247 610 0-
$a High temperature 610 0-
$a Fracture surface 610 0-
$a S-N curve 700 -1
$3 cav_un_auth*0249022 $a Šmíd $b Miroslav $i Nízkocyklová únava $j Low cycle fatigue $p UFM-A $w High Cycle Fatigue Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0101287 $a Kunz $b Ludvík $i Vysokocyklová únava $j High cycle fatigue $p UFM-A $w High Cycle Fatigue Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0101268 $a Hutař $b Pavel $i Vysokocyklová únava $j High cycle fatigue $p UFM-A $w High Cycle Fatigue Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0297755 $a Hrbáček $b K. $y CZ $4 070
Number of the records: 1