Ductile-brittle behavior of (001)[110] nano-cracks in bcc iron.
[Tvárně-křehké chování nano-trhlin (001)[110] v alfa železe.]
Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. Roč. 387, 389C (2004), s. 414-418. ISSN 0921-5093. E-ISSN 1873-4936.
[ICSMA-13. Budapest, 25.08.2003-30.08.2003]
R&D Projects: GA AV ČR IAA2076201; GA MŠMT ME 504
Grant - others:NSF(US) 0000142
Institutional research plan: CEZ:AV0Z2076919
Keywords : crack * stability * twins
Subject RIV: JG - Metallurgy
Impact factor: 1.445, year: 2004

Atomistic simulations and stress analysis of crack behavior loaded in Mode I show thatgeneration of unstable stacking faults at the crack tip of a relatively long crack (16 nm) cannot prevent unstable crack extension at the Griffith level. A crack of smaller dimensions (4 nm) produces twinning on the 111{112} slip system. It causes a a slow ductile growth during subsequent quasi-static loading. The influence of the T-stress on the shear processes at the crack tip and crack stability is discussed.

Atomární simulace a napěťová analýza chování trhlin zatížených v módu I ukazují, že generace nestabilních vrstevných chyb u kořene relativně dlouhé trhliny (16 nm) nemůže zabránit nestabilnímu růstu trhliny při kritickém Griffithově zatížení. Jiná trhlina menších rozměrů (4 nm) generuje dvojčata ve skluzových systémech 111{112}. To způsobuje pomalý plastický růst trhliny při dalším kvazi-statickém zatížení. Je diskutován vliv T-napětí na smykové procesy u kořene trhliny a je diskutována stabilita trhliny.