Preparation of Ti2C MXene phase by ion beam sputtering and ion irradiation

0524055 - ÚJF 2021 RIV NL eng J - Journal Article
Horák, Pavel - Bakardjieva, Snejana - Vacík, Jiří - Rui, X. - Klie, R.
Preparation of Ti2C MXene phase by ion beam sputtering and ion irradiation.
Nuclear Instruments & Methods in Physics Research Section B. Roč. 469, č. 4 (2020), s. 49-51. ISSN 0168-583X. E-ISSN 1872-9584
R&D Projects: GA ČR(CZ) GA18-21677S
Institutional support: RVO:61388980 ; RVO:61389005
Keywords : MXenes * Ti2C * ion beam sputtering * ion irradiation
OECD category: Nuclear physics; Inorganic and nuclear chemistry (UACH-T)
Impact factor: 1.377, year: 2020
Method of publishing: Limited access
https://doi.org/10.1016/j.nimb.2020.02.010

Thin titanium carbide films were prepared by ion beam sputtering of titanium and graphite targets followed by thermal annealing at 600 degrees C in vacuum and irradiation by Ar+ ions up to a fluence of 10(15) ions/cm(2). The stoichiometry of the films was analyzed by RBS and NRA methods, it was found to be Ti2.2C. The crystalline structure of the films was analyzed by STEM and EELS microscopic methods: before irradiation it was mostly amorphous with crystalline parts and visible network of micro-voids, crystallization and formation of laminar structure was observed after irradiation. The irradiated part showed corrugated surface morphology and a dense network of nano-openings. The thickness of the films increased from ca 67 nm to ca 83 nm. Obviously, the effect of the ion irradiation promoted the recrystallization and self-organization of the structure, resulting in the nanolaminar phase of Ti2C.
Permanent Link: http://hdl.handle.net/11104/0308363