Transferability of fracture mechanical data from sub-sized three point bend specimens
- 1.0370106 - ÚFM 2012 RIV IE eng O - Others
Stratil, Luděk - Čermák, Martin - Hadraba, Hynek - Dlouhý, Ivo
Transferability of fracture mechanical data from sub-sized three point bend specimens.
2011
R&D Projects: GA ČR(CZ) GAP107/10/0361; GA ČR GD106/09/H035
Institutional research plan: CEZ:AV0Z20410507
Keywords : three-point-bend specimen * stress-strain state * Eurofer´97 * J-integral
Subject RIV: JL - Materials Fatigue, Friction Mechanics
The contribution deals with FEA of stress state in sub-sized pre-cracked three-point bend specimen with dimensions 3×4×27 mm3. In the experimental part the true stress-true strain curve was obtained from tensile test from Eurofer´97 steel. Next, the static three point bend tests with different crack lengths were carried out on plain and side-grooved specimens. The tests were simulated using ABAQUS 6.10. For comparison, models of pre-cracked standard and Charpy specimen were also created. The stress level below the crack tip for both KLST and Charpy specimen decrease more extensively than for standard specimen indicating the constraint loss. The decrease of the stress level and thus constraint loss is the highest just for the smallest specimen. The different crack lengths have no influence on the stress level at the crack tip. The side grooving enabled to maintain the stress level at the crack tip along the thickness but does not have effect on the maximum value of the stress.