Slip activity in molybdenum single crystals compressed at77 K
- 1.0495464 - ÚFM 2019 RIV GB eng J - Journal Article
Gröger, Roman - Chlup, Zdeněk - Kuběna, Ivo - Kruml, Tomáš
Slip activity in molybdenum single crystals compressed at77 K.
Philosophical Magazine. Roč. 98, č. 30 (2018), s. 2749-2768. ISSN 1478-6435. E-ISSN 1478-6443
R&D Projects: GA MŠMT(CZ) LQ1601; GA ČR(CZ) GA16-13797S
Institutional support: RVO:68081723
Keywords : molybdenum * slip traces * plasticity * low temperature * cross-slip
OECD category: Condensed matter physics (including formerly solid state physics, supercond.)
Impact factor: 1.855, year: 2018
High-purity single crystals of molybdenum of five different orientations were compressed at 77 K to plastic strains between 3% and 4% to investigate the initial stage of plastic flow in these metals. Electron back-scatter diffraction was used to determine the sample orientations before and after deformation to quantify the magnitude and direction of lattice rotation. The slip trace analysis on two perpendicular faces of each prismatic specimen, made using the Nomarski interference contrast, reveals that the slip morphology depends strongly on the orientation of the applied load. The sample oriented near the [001] axis and that of the centre-triangle orientation exhibited sharp slip traces on (101) and (101) planes, whereas the samples oriented near the [011] -[111] edge of the triangle yielded by macroscopic slip on a series of high-index planes. The orientations of observed slip traces were compared with theoretical predictions of slip activity of the twelve {110} 111 slip systems made by the Schmid law and using the effective yield criterion developed previously using molecular statics simulations of an isolated 1/2[111] screw dislocation under stress