The shape of extrusions and intrusions and initiation of stage I fatigue cracks

0332429 - ÚFM 2010 RIV CH eng J - Journal Article
Polák, Jaroslav - Man, Jiří - Vystavěl, T. - Petrenec, Martin
The shape of extrusions and intrusions and initiation of stage I fatigue cracks.
[Tvar extruzí a intruzí a iniciace primárních únavových trhlin.]
Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. Roč. 517, 1-2 (2009), s. 204-211. ISSN 0921-5093. E-ISSN 1873-4936
R&D Projects: GA ČR GA106/06/1096; GA ČR GA101/07/1500
Institutional research plan: CEZ:AV0Z20410507
Keywords : Extrusion * Intrusion * Fatigue crack initiation * Stainless steel
Subject RIV: JL - Materials Fatigue, Friction Mechanics
Impact factor: 1.901, year: 2009

Scanning electron microscopy (SEM) combined with local milling by focused ion beam (FIB) was used to study the true shape of the relief developed on the surface of polycrystalline 316L steel cycled with constant plastic strain amplitude. Localization of the cyclic strain to persistent slip bands results in early formation of persistent slip markings. The evolution of the early relief formation is reported using the observation on two perpendicular surfaces. The observed configurations of extrusions and intrusions are discussed and compared with predictions of the latest models of fatigue crack initiation. The prominent role of intrusions in fatigue crack initiation is emphasized.

Byl studován skutečný tvar povrchového reliéfu polykrystalické oceli 316L cyklicky namáhané konstantní amplitudou plastické deformace pomocí rastrovacího mikroskopu a fokuzovaného svazku iontů (FIB).Lokalizace cyklické deformace do perzistentních skluzových pásů ná za následk vznik perzistentních skluzových stop. Pozorované konfigurace extruzí a intruzí na dvou kolmých plochách byly diskutovány a srovnány s nedávnými modely iniciace únavových trhlin.