0103497 - UT-L 20040003 RIV NL eng J - Journal Article
Beltz, G. E. - Machová, Anna
Effect of T-stress on dislocation emission in iron.
[Vliv T-napětí na emisi dislokací v železe.]
Scripta Materialia. Roč. 50, č. 50 (2004), s. 483-487. ISSN 1359-6462. E-ISSN 1872-8456
R&D Projects: GA AV ČR IAA2076201; GA MŠMT ME 504
Grant - others:NSF(US) CMS0000142
Institutional research plan: CEZ:AV0Z2076919
Keywords : dislocation * emission * iron
Subject RIV: JG - Metallurgy
Impact factor: 2.112, year: 2004

Continuum predictions for dislocation emission from a crack tip loaded under mode I, biaxial conditions, are compared with atomistic results for bcc iron. The simulations validate the continuum prediction that, as the T-stress increases, so does the threshold for dislocation nucleation; hence, the propensity for brittle response increases.

Predikce kontinua o emisi dislokací od kořene trhliny, zatíženého v tahovém módu I a biaxiálně, jsou porovnány s atomárními výsledky pro alfa železo. Atomární simulace potvrzují predikci kontinua, že se vzrůstem T-napětí se zvyšuje práh pro nukleaci dislokací a tudíž pravděpodobnost křehkého lomu vzrůstá.
Permanent Link: http://hdl.handle.net/11104/0010804