Fatigue properties and crack growth in Eurofer steel

0332819 - ÚFM 2010 RIV SK eng J - Journal Article
Kuběna, Ivo - Kruml, Tomáš
Fatigue properties and crack growth in Eurofer steel.
[Únavové vlastnosti a růst trhiln v oceli Eurofer 97.]
Materiálové inžinierstvo - Materials Engineering. Roč. 16, 3a (2009), s. 32-36. ISSN 1335-0803
R&D Projects: GA ČR GA106/09/1954
Institutional research plan: CEZ:AV0Z20410507
Keywords : low cycle fatigue * short crack propagation * fatigue softening
Subject RIV: JL - Materials Fatigue, Friction Mechanics

Cyclic plastic response of the Eurofer reduced activation ferritic-martensitic steel at room temperature was studied. Strain amplitude was kept constant during cycling. The softening curves in two representation were obtained. The fatigue life curve in NF = f(ea) representation and the cyclic stress-strain curve were determined. The main part of the study was focused on surface relief observation: determination of crack nucleation sites and kinetics of crack growth. The crack growth coefficient kg was measured, allowing the fatigue life predictions based on the kinetics of short crack growth. The fracture surfaces were observed using scanning electron microscopy (SEM). Nucleation sites, striation and other typical fatigue features were detected.

Byla studována cyklická odezva feriticko-martenzitické oceli Eurofer, zkoušky byly prováděny v řízení konstantní celkové deformace. Byly získány křivky únavového zpevnění a změkčení ve dvou reprezentacích. Byly získány křivky únavového života. Hlavní cíl práce byl zaměřen na pozorování iniciace krátkých trhlin a jejich následném růstu. Byly pozorovány lomové plochy a nalezeny typické prvky únavového poškození.