Observation of record flux pinning in melt-textured NEG-123 superconductor doped by Nb, Mo, and Ti nanopaticles

0330011 - FZÚ 2010 RIV NL eng J - Journal Article
Muralidhar, M. - Tomita, M. - Jirsa, Miloš - Sakai, N. - Murakami, M. - Hirabayashi, I.
Observation of record flux pinning in melt-textured NEG-123 superconductor doped by Nb, Mo, and Ti nanopaticles.
[Rekordní upnutí vírů v texturovaném supravodiči NEG-123 dopovaném nanočásticemi Nb, Mo a Ti.]
Physica. C. Roč. 469, 15-20 (2009), s. 1196-1199. ISSN 0921-4534. E-ISSN 1873-2143
R&D Projects: GA ČR GA202/08/0722
Institutional research plan: CEZ:AV0Z10100520
Keywords : NEG-123 * critical currents * record vortex pinning * high-Tc superconductors * levitation
Subject RIV: BM - Solid Matter Physics ; Magnetism
Impact factor: 0.723, year: 2009

Doping of the ternary NEG-123 superconductor by Nb₂O₅, MoO₃ and TiO₃ nanoparticles led to record values of the critical current density giving evidence of up to now most effective vortex pinning in bulk superconductors. The optimum concentration of all three dopands was 0.1 mol% in the Nb₂O₅ doped sample the remnant Jc achieved 925 kA/cm² at 65 K, 640 kA/cm² at 77 K, and 100 kA/cm² at 90.2 K. This enables a steady levitation up to vicinity to the critical temperature of this material.

Dopováním ternárního supravodiče NEG-123 nanočásticemi Nb₂O₅, MoO₃ a TiO₃ bylo dosaženo rekordních hodnot kritické proudové hustoty svědčících o dosud nejefektivnějším upnutí vírů v objemných supravodičích. Optimální koncentrace u všech dopandů byla 0.1 mol%. U vzorku dopovaného Nb₂O₅ bylo dosaženo Jc v remanentním stavu 925 kA/cm2 při 65 K, 640 kA/cm2 při 77 K a 100 kA/cm2 při 90.2 K, což umožňuje stabilní levitaci až do blízkosti kritické teploty tohoto materiálu.