0026174 - ÚFM 2006 RIV SK eng J - Journal Article
Kloc, Luboš - Fiala, J.
Viscous creep in metals at intermediate temperatures.
[Viskózní creep kovů při středních teplotách.]
Kovové materiály. Roč. 43, č. 2 (2005), s. 105-112. ISSN 0023-432X. E-ISSN 1338-4252
R&D Projects: GA AV ČR(CZ) IAA2041101
Institutional research plan: CEZ:AV0Z20410507; CEZ:AV0Z2041904
Keywords : creep * heat resistant steel
Subject RIV: JG - Metallurgy
Impact factor: 0.973, year: 2005

Creep at stresses below 100 MPa and temperatures from 600°C to 750°C was investigated on two types of creep resistant steels: ferritic-martensitic P-91 type and austenitic AISI-316H type. Evidences were found that the creep process at low stresses is very different from that at high stresses in many features. The most important is that the efficiency of strengthening microstructural elements drops down drastically at low stresses.Deformation mechanism of the low stress creep remains unclear, but it is very sensitive to the fine microstructural changes which cannot be simply detected by optical and electron metallography.

Creep feritické oceli typu P-91 a austenitické oceli typu AISI-316H byl zkoumán při napětích pod 100 MPa a teplotách 600°C až 750°C. Byly získány důkazy, že proces creepové deformace při nízkých napětích je velmi odlišný od deformace při vyšších napětích v mnoha ohledech. Nejdůležitější je výrazné snížení účinnosti zpevňujících prvků mikrostruktury při nízkých napětích. Deformační mechanismus creepu při nízkých napětích zůstává nejasný, je však velmi citlivý na malé změny mikrostruktury, které nelze jednoduše detekovat prostředky optické a elektronové metalografie.