0024745 - ÚFM 2006 RIV CZ eng C - Conference Paper (international conference)
Zábranský, Karel - Jirásková, Yvonna
An influence of thermal treatment on mechanical properties of FeNiB amorphous alloys.
[Vliv tepelného namáhání na mechanické vlastnosti FeNiB amorfní slitiny.]
JUNIORMAT´05. Brno: VUT, FSI, 2005, s. 27-30. ISBN 80-214-2984-4.
[Juniormat '05. Brno (CZ), 20.09.2005-21.09.2005]
Institutional research plan: CEZ:AV0Z20410507
Keywords : Amorphous * tensile testing * microhardness
Subject RIV: BM - Solid Matter Physics ; Magnetism

An influence of thermal treatment in the temperature range of 150 - 350 °C on the structural and mechanical properties of an amorphous FeNiB alloy is investigated. The high tensile strength of 2200 MPa in the as-prepared amorphous state slightly decreases with increasing temperature of annealing up to approximately 200 °C in opposite to microhardness where an increase is observed. Above 200 °C a pronounced deterioration of both characteristics reflect the embrittlement of amorphous structure without any indications of crystallization.

Vliv tepelného namáhání v teplotním intervalu 150 - 350 °C na změny struktury a mechanických vlastností je studován na vzorcích FeNiB s amorfní strukturou. Vysoká pevnost v tahu, 2200 MPa, naměřená u vzorku v původním amorfním stavu mírně klesá s rostoucí teplotou žíhání vzorků do přibližně 200 °C na rozdíl od mikrotvrdosti, u níž je pozorován růst. Nad touto teplotou však dochází k výraznému zhoršení obou vlastností vlivem křehnutí amorfní struktury bez jakýchkoliv známek krystalizace.